Aluminum Fence Colors

Installing residential, commercial, and industrial aluminum fencing doesn’t have to mean sacrificing appearance for function. Your fence is also part of your property, so we give you the freedom to choose its colors and finish. GreatFence.com offers a selection of aluminum fence colors, allowing you to complement it with the style of your property.

High Performance Standard

Our aluminum gates and fencing has passed the standards of the American Architectural Manufacturers Association (AAMA), from pretreatment to weathering resistance.  Our products have been through different types of tests to make sure that we live up to our promise.  Check the table at the end of this page to see how much better we perform compared to our competitors. 

Color and Finish Selection

Choose from our range of aluminum fence colors and finishes.  We have gold, bronze, white, black, hunter green, and sandstone gloss.  If you prefer a flat finish, we also offer satin white, bronze, khaki, and black.  No matter what you order, you’ll receive a lifetime warranty.

Maintenance-free Fencing

We understand how frustrating it is to see fences losing their color due to fading, chipping, and cracking.  Our aluminum fence colors at GreatFence.com keep you away from this scenario.  We offer products that need little to no maintenance, so you’ll never repaint your fences… ever.

For more than 10 years, GreatFence.com has been one of the leading providers of high standard, powder coated aluminum fences and gates.  Give our online sales division a call at 845-443-7242 to know your choices.

Colored Ball Caps
  Testing Competition
AAMA 2603
GREATFENCE.com
AAMA 2604-5
 


Pre-
treatment

Metal Preparation
and Pretreatment
Multi-Stage Cleaning and Pretreatment Multi-Stage Cleaning and Pretreatment
Pretreatment Type Chemical Conversion Coating Chrome or Non-Chrome Chemical
Conversion Coating
Pretreatment
Coating Weight
None Specified Chrome @ 30mg/ft² Minimum;
Non-Chrome per Supplier’s Specs
 

 

Paint Film

Dry Film
Thickness
0.8 mils min. 1.2 mils (for Multi-coat, 1.0 mil Topcoat
min & 0.3+/-0.1 mil Primer
Sealant
Compatibility
Meets AAMA 800 Meets AAMA 800
Specular Gloss +/-5 Units of Specification
(high = 80+, medium+20-79, low 19-)
+/-5 Units of Specification
(high = 80+, medium+20-79, low 19-)
Dry Film
Hardness
H Minium F Minimum
 

 

Adhesion

Dry Adhesion 0% Failure (No Loss) 0% Failure (No Loss)
Wet Adhesion 0% Failure (No Loss) 0% Failure (No Loss)
Boiling Water
Adhesion
None Specified 0% Failure (No Loss)
Impact
Resistance
No Removal of Film from Substrate No Removal of Film from Substrate
Abrasion
Resistance
None Specified Abrasion Coefficient Value = 20 Min
 



Chemical
Resistance

Muriatic Acid
Resistance
15 Minute Exposure: No Blistering or Visual Change for AAMA 2603, 2604, 2605
Mortar
Resistance
24 Hour Exposure: No Loss of Film Adhesion or Visual Change for AAMA 2603, 2604, 2605
Nitric Acid
Resistance
None Specified 30 Minute Exposure: 5 Delta E (Hunter)
Maximum Color Change
Detergent
Resistance
72 Hour Exposure: No Loss of Film Adhesion, No Blistering or
No Significant Visual Change for AAMA 2603, 2604, 2605
Window
Cleaner
Resistance
None Specified 24 Hour Exposure: No Blistering
or Visual Change



Corrosion
Resistance
Humidity Resistance 1500 Hours: No More than "Few" Blisters
Size 8, Figure #4 (ASTM D 714)
3000 Hours: No More than "Few" Blisters
Size 8, Figure #4 (ASTM D 714)

Salt Spray Resistance
1500 Hours of Salt Solution:
Minimum Rating of 7 on Scribe or Cut Edges;
Minimum Blister Rating of
8 in the Field (ASTM D 1654)
3000 Hours of Salt Solution:
Minimum Rating of 7 on Scribe or Cut Edges;
Minimum Blister Rating of
8 in the Field (ASTM D 1654)




Weathering
Resistance

Accelerated
Exposure
1000 Hours in Atlas Type "XW" Weatherometer:
No Adhesion Loss;
Slight Chalking or Color Change
 

None Specified


Outdoor
Exposure

1 Year South Florida: No Adhesion Loss;
Slight Chalking or Fading
5 Years South Florida: 5 Delta E
(Hunter) Maximum Color Change;
Chalking < 8 (ASTM D 4214);
Gloss Retention > 30%
Erosion Resistance < 10% Film Loss